Autori: C. Zhang , H. Liao , W.-Y. Li , G. Zhang, C.-J. Li, C.-X. Li , X.-J. Ning, C. Coddet,
Editorial: Journal of Thermal Spray Technology, 15(4), p.598-603, 2006.
Yttria doped zirconia has been widely employed as electrolyte materials for solid oxide fuel cells (SOFCs). Plasma spraying is a cost-effective process to deposit YSZ electrolyte. In this study, the 8 mol % Y2O3 stabilized ZrO2 (YSZ) layer was deposited by low pressure plasma spraying (LPPS) and atmospheric plasma spraying (APS) with fused-crushed and agglomerated powders to examine the effect of spray method and particle size on the electrical conductivity and gas permeability of YSZ coating. The microstructure of YSZ coating was characterized by scanning electron microscopy and X-ray diffraction analysis. The results showed that the gas permeability was significantly influenced by powder structure. The gas permeability of YSZ coating deposited by fused-crushed powder is one order lower in magnitude than that by agglomerated powder. Moreover, the gas permeability of YSZ deposited by LPPS is lower than that of APS YSZ. The electrical conductivity of the deposits through thickness direction was measured by potentiostat/galvanostat based on three-electrode assembly approach. The electrical conductivity of YSZ coating deposited by LPPS with fused-crushed powder of small particle size was 0.043 S cm-1 at 1000°C, which is about 20% higher than that of APS YSZ with the same powder.
Cuvinte cheie: plasma spraying, solid oxide fuel cell, yttria stabilized zirconia, coating