Autori: Gabriela Carja, (autor de corespondenta) Kameshima, Y., Okada, K.
Editorial: MICROPOROUS AND MESOPOROUS MATERIALS (ELSEVIER PRESS, 115, p.541-547, 2008.
Rezumat:
Nanostructured catalysts derived from nanoparticles of iron or vanadium oxides supported on the matrices of iron substituted hydrotalcite-like anionic clays (LDHs) have been obtained and tested in the process of ethylbenzene dehydrogenation to styrene. A simple synthesis method based on the LDHs “memory effect” has been used to prepare the new oxides-anionic clay structures. TEM analysis shows that on the typical FeLDH particles (average size equal to 75 nm) smaller nanoparticles are supported; their average size is equal to 7 and 11 nm for Fe/FeLDH and V/FeLDH respectively. XPS analysis indicates the presence of Fe2O3 and V2O3 on the surface of the supported LDHs. N2 adsorption at 77 K reveals that the supported anionic clays have less accentuated mesoporous properties in comparison to the parent FeLDH matrix. The catalytic behavior of the samples is a function of the nature of the supported nanoparticles.
Cuvinte cheie: nanostructured catalysts