Autori: A. M. Chinie, A. Stefan, S. Georgescu, O. Toma, E. Borca, M. Bercu
Editorial: Journal of Optoelectronics and Advanced Materials, 8, p.95-98, 2006.
Rezumat:
Nanocrystalline YAG powders doped with Er3+, Eu3+ or Tb3+ were synthesized through a citrate-nitrate sol-gel process. Thermal treatments were applied at successively increasing temperatures in the interval 600-1400°C. The structural transformations were monitored by XRD, FT-IR and optical spectroscopy. A pure garnet phase was observed for annealing temperatures higher than 930°C.
Cuvinte cheie: Nanocristale, YAG, Eu3+, Er3+, Tb3+, Metoda Sol-Gel // Nanocrystals, YAG, Eu3+, Er3+, Tb3+, Sol-Gel Method